In the case of alkaline CaO coexisting with Cr_2O_3, the production of CaCrO_4, a Cr~(6+) compound, is stimulated as the stable phase in the temperature range less than 1000°C in air atmosphere1'. On the contrary, CaCr_2O_4, a Cr~(3+)+ compound, becomes the stable phase at more than 1000°C in air atmosphere. However, in the case of the presence of Al_2O_3 together with CaO and Cr_2O_3 there is a possibility that the Cr~(6+) compound CaCrO_4 is produced even at temperatures higher than 1000°C, although there is no literature concerning details of this behavior. This research investigates the amount of Cr~(6+) compound and mineral phases generated at 1450°C in reactions between constituents in the CaO-system.