作者：RYOUZOU IKUTA;YOSHIMASA MIYAGISHI;KAZUKI NISHIDA;

作者单位：AGC Ceramics Co.,-Ltd.;AGC Ceramics Co.,-Ltd.;AGC Ceramics Co.,-Ltd.

刊名：Journal of the Technical Association of Refractories

ISSN：0285-0028

出版年：2009-01-05

卷：29

期：2

起页：166

止页：166

分类号：TQ175

语种：英文

关键词：

内容简介

Non-cement type and silica-less castables for use as monolithic refractories for wastes melting furnace were produced and corrosion resistances were measured. As a result, it was clarified that newly developed castable had higher corrosion resistance even with lower MgO composition than the traditional low cement castable. Further work will focus on improving the properties in order to develop Cr-free castables, which are equivalent to Cr_2O_3 containing castable.